Unveiling FGS 70-2 Steel Grade: A Revolutionary Solution for High-Stress Applications

Unveiling FGS 70-2 Steel Grade: A Revolutionary Solution for High-Stress Applications

Unveiling FGS 70-2 Steel Grade: A Revolutionary Solution for High-Stress Applications


1. Material: FGS 70-2 Steel Grade
2. Application: High-stress applications requiring exceptional strength and durability
3. Mechanical Properties:
– Ultimate Tensile Strength: 70,000 psi (480 MPa)
– Yield Strength: 60,000 psi (410 MPa)
– Elongation: 20%
– Reduction in Area: 40%
– Hardness: 220 HB
4. Chemical Composition:
– Carbon (C): 0.25%
– Manganese (Mn): 1.50%
– Phosphorus (P): 0.04%
– Sulfur (S): 0.05%
– Silicon (Si): 0.50%
– Chromium (Cr): 0.30%
– Nickel (Ni): 0.30%
– Copper (Cu): 0.25%
5. Heat Treatment: Quenched and Tempered to achieve desired mechanical properties
6. Surface Finish: Mill finish with no surface defects or imperfections
7. Dimensions: Available in various sizes and forms (e.g., sheets, plates, bars, tubes) to suit different application requirements
8. Corrosion Resistance: Good resistance to atmospheric and mild chemical corrosion
9. Weldability: Excellent weldability with appropriate welding procedures and precautions
10. Certification and Standards: Compliant with industry standards and certifications for high-stress applications (e.g., ASTM, ISO)

The FGS 70-2 Steel Grade is a revolutionary solution specifically designed for high-stress applications that demand exceptional strength, durability, and performance. With its carefully engineered mechanical properties and precise chemical composition, this steel grade offers superior tensile and yield strength, ensuring reliable performance even under extreme conditions.

The mechanical properties of FGS 70-2 Steel Grade highlight its exceptional strength, including an ultimate tensile strength of 70,000 psi and a yield strength of 60,000 psi. This steel grade also exhibits a significant elongation of 20% and a reduction in area of 40%, indicating its ability to withstand heavy loads and deformation without failure. With a hardness of 220 HB, FGS 70-2 Steel Grade provides excellent resistance to wear and abrasion.

The chemical composition of FGS 70-2 Steel Grade has been carefully formulated to enhance its mechanical properties and ensure optimal performance. With controlled levels of carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, and copper, this steel grade exhibits excellent machinability, weldability, and corrosion resistance.

To achieve the desired mechanical properties, FGS 70-2 Steel Grade undergoes a quenching and tempering heat treatment process. This process improves the steel’s strength, toughness, and hardness, making it suitable for high-stress applications.

With its exceptional mechanical properties, precise chemical composition, and revolutionary design, FGS 70-2 Steel Grade is an ideal solution for demanding applications such as structural components, heavy machinery, construction equipment, and other high-stress environments.

Note: The specific mechanical properties and chemical composition mentioned above may vary depending on the manufacturer and specific product requirements. It is essential to consult the product data sheet or contact the manufacturer for accurate and up-to-date information.
FGS 70-2 Steel grade