The Rising Demand for X12CrS13 Steel Grade in Various Industries

Specification:

– X12CrS13 is a martensitic stainless steel grade that offers good corrosion resistance and high strength, making it suitable for various industrial applications.
– It is commonly used in the manufacturing of components for the automotive, aerospace, and oil and gas industries.
– The steel grade conforms to the European standard EN 10088-1.
– X12CrS13 has a nominal composition of 0.10% carbon, 1.00% silicon, 1.00% manganese, 13.00% chromium, and 0.030% sulfur.
– The steel grade is available in various forms, including bars, sheets, and plates, with dimensions and specifications tailored to meet the specific requirements of different industries.
– X12CrS13 offers good machinability, allowing for easy shaping and forming of components.
– The steel grade can be heat treated to enhance its mechanical properties and improve its wear resistance.
– X12CrS13 exhibits excellent resistance to corrosion in both fresh and saltwater environments, making it suitable for applications that require exposure to moisture or corrosive substances.
– It retains its mechanical properties at elevated temperatures, making it suitable for high-temperature applications.
– X12CrS13 can be welded using conventional welding techniques, and its weldability is comparable to other stainless steel grades.
– The steel grade undergoes rigorous quality control measures to ensure that it meets industry standards and customer specifications.
– X12CrS13 is cost-effective compared to other stainless steel grades, making it a preferred choice for various industries.

Mechanical Properties:

– X12CrS13 has a tensile strength of approximately 650 to 850 MPa, depending on the heat treatment conditions.
– It has a yield strength of around 450 to 650 MPa.
– The steel grade exhibits good hardness, typically ranging from 20 to 30 HRC (Rockwell Hardness Scale).
– X12CrS13 offers excellent impact strength, making it suitable for applications subjected to high-stress conditions.
– It has a coefficient of thermal expansion similar to other martensitic stainless steels.
– The steel grade exhibits good fatigue resistance, allowing it to withstand cyclic loading without experiencing significant degradation in performance.

Chemical Composition:

– X12CrS13 has a chemical composition that primarily consists of:
– Carbon: 0.10%
– Silicon: 1.00%
– Manganese: 1.00%
– Chromium: 13.00%
– Sulfur: 0.030%
– Iron: Remaining balance

– Additionally, minor elements such as phosphorus, nickel, and copper may be present in trace amounts.

Note: The specifications, mechanical properties, and chemical composition mentioned above are based on general industry standards and may vary depending on specific product forms and manufacturers. Users should consult the relevant technical data sheets or contact suppliers for precise information.
X12CrS13 Steel grade