Unveiling the Exceptional Corrosion Resistance of 14MoV63 Steel Grade

specification of 14MoV63 Steel Grade:
– Corrosion Resistance: Exceptional
– Durability: High
– Steel Type: Martensitic Alloy Steel
– Nominal Composition:
– Carbon (C): 0.1%
– Silicon (Si): 0.5%
– Manganese (Mn): 0.5%
– Chromium (Cr): 2.5%
– Molybdenum (Mo): 0.63%
– Vanadium (V): 0.1%
– Iron (Fe): Remaining
– Hardness: 190-220 HBW
– Yield Strength: 490 MPa
– Tensile Strength: 680 MPa
– Elongation: 22%
– Impact Strength (Charpy V-notch): 34 J @ 20°C
– Heat Treatment: Normalized and Tempered
– Weldability: Good

mechanical properties of 14MoV63 Steel Grade:
– Ultimate Tensile Strength: 680 MPa
– Yield Strength: 490 MPa
– Elongation: 22%
– Impact Strength (Charpy V-notch): 34 J @ 20°C
– Hardness: 190-220 HBW
– Modulus of Elasticity: 200 GPa
– Poisson’s Ratio: 0.3
– Fatigue Strength (at 10^7 cycles): 400 MPa

chemical composition of 14MoV63 Steel Grade:
– Carbon (C): 0.1%
– Silicon (Si): 0.5%
– Manganese (Mn): 0.5%
– Phosphorus (P): 0.03% (maximum)
– Sulfur (S): 0.02% (maximum)
– Chromium (Cr): 2.5%
– Molybdenum (Mo): 0.63%
– Vanadium (V): 0.1%
– Iron (Fe): Remaining

Note: The above specifications are approximate values and may vary slightly depending on manufacturing processes and standards. It is always recommended to refer to the manufacturer’s datasheet for accurate and up-to-date information.
14MoV63 Steel grade