X5CrNiMo1810 Steel Grade: From Fabrication to Final Product

Specifications of X5CrNiMo1810 Steel Grade: From Fabrication to Final Product:

1. Type: X5CrNiMo1810 is a stainless steel grade with high corrosion resistance and good mechanical properties. It belongs to the austenitic stainless steel family and is commonly known as AISI 316 or ASTM A193 Grade B8M.

2. Fabrication: X5CrNiMo1810 can be fabricated using standard methods such as hot and cold forming, machining, welding, and heat treatment. It has good workability and can be easily shaped into various components.

3. Final Product: X5CrNiMo1810 is widely used in various industries for manufacturing components such as pipes, fittings, valves, flanges, fasteners, and equipment for chemical processing, food processing, pharmaceuticals, power generation, and marine applications. It is also used in architectural and decorative applications.

Mechanical Properties of X5CrNiMo1810 Steel Grade: From Fabrication to Final Product:

1. Tensile Strength: The tensile strength of X5CrNiMo1810 steel grade typically ranges from 500 to 700 MPa (Megapascals), depending on the heat treatment and manufacturing process.

2. Yield Strength: The yield strength of X5CrNiMo1810 steel grade is generally around 200 to 400 MPa, depending on the tempering temperature and annealing conditions.

3. Elongation: X5CrNiMo1810 exhibits high elongation, typically greater than 40%, which indicates good ductility and the ability to withstand deformation before breaking.

4. Hardness: X5CrNiMo1810 steel grade has a hardness range of 170 to 220 HB (Brinell hardness) or 85 to 95 HRB (Rockwell hardness). It can be further hardened by cold working or heat treatment if required.

Chemical Composition of X5CrNiMo1810 Steel Grade: From Fabrication to Final Product:

1. Carbon (C): The carbon content in X5CrNiMo1810 is typically less than 0.08%, which ensures good weldability and avoids carbide precipitation during welding.

2. Chromium (Cr): The chromium content in X5CrNiMo1810 is around 16 to 18%, providing excellent corrosion resistance, especially in oxidizing environments.

3. Nickel (Ni): The nickel content in X5CrNiMo1810 is approximately 10 to 14%, which contributes to the overall corrosion resistance and enhances the material’s toughness and ductility.

4. Molybdenum (Mo): X5CrNiMo1810 contains about 2 to 3% molybdenum, which enhances its corrosion resistance, particularly in chloride-containing environments such as marine applications.

5. Other Elements: X5CrNiMo1810 may contain small amounts of other elements such as silicon (Si), manganese (Mn), sulfur (S), phosphorus (P), and nitrogen (N), which are controlled within specific limits to ensure consistent mechanical properties and corrosion resistance.
X5CrNiMo1810 Steel grade